Component - Photovoltaic Polymeric Materials
E316895
3M COMPANY
3M CENTER, ST PAUL MN 55144
3M(TM) Scotchshield (TM) Film 17HTT(C)
TFE/PET/EVA, Photovoltaic Backsheets, furnished as sheets
Air-side
Cell-side
Nom Thk
Flame
RTI
RTI
Color
Color
(mm)
Class
HWI
HAI
Elec
Str
WT
WT
0.41
RP25
-
-
-
-
Comparative Tracking Index (CTI):
-
Inclined Plane Tracking (IPT):
-
Dielectric Strength (kV/mm):
-
Volume Resistivity (10
x
ohm-cm) :
-
High-Voltage Arc Tracking Rate (HVTR):
-
High Volt, Low Current Arc Resis (D495):
-
Dimensional Stability (%):
-
(C) -
Radiant Panel rating applies only when a glass substrate (3.175 mm minimum) is adhered to one side of the material, using 0.46 mm encapsulant Saint-Gobain Ceramics and Plastics (E330778). Test Results for Radiant Panel obtained using ASTM E162-11
ANSI/UL 94 small-scale test data does not pertain to building materials, furnishings and related contents. ANSI/UL 94 small-scale test data is intended solely for determining the flammability of plastic materials used in the components and parts of end-product devices and appliances, where the acceptability of the combination is determined by UL.
Report Date:
2009-07-16
Last Revised:
2012-07-25
© 2013 UL LLC
IEC and ISO Test Methods
Thickness
Test Name
Test Method
Units
Tested (mm)
Value
Flammability
IEC 60695-11-10
Class (color)
0.41
RP25WT, WT
Glow-Wire Flammability (GWFI)
IEC 60695-2-12
C
-
-
Glow-Wire Ignition (GWIT)
IEC 60695-2-13
C
-
-
IEC Partial Discharge
IEC 61730-2, MST 15
Max System Voltage (V)
-
-
IEC Comparative Tracking Index
IEC 60112
Volts (Max)
-
-
IEC Ball Pressure
IEC 60695-10-2
C
-
-
ISO Heat Deflection (1.80 MPa)
ISO 75-2
C
-
-
ISO Tensile Strength
ISO 527-2
MPa
-
-
ISO Flexural Strength
ISO 178
MPa
-
-
ISO Tensile Impact
ISO 8256
kJ/m
2
-
-
ISO Izod Impact
ISO 180
kJ/m
2
-
-
ISO Charpy Impact
ISO 179-2
kJ/m
2
-
-
© 2013 UL LLC
The materials covered in this database are incomplete in certain constructional features or restricted in performance capabilities and are intended for use as components of complete equipment submitted for investigation rather than for direct separate installation in the field. THE FINAL ACCEPTANCE OF THE COMPONENT IS DEPENDENT UPON ITS INSTALLATION AND USE IN COMPLETE PRODUCTS SUBMITTED TO UNDERWRITERS LABORATORIES.